| Název | EN norma | AWS norma | Mechanické vlastnosti | Průměr |
Familiarc DW-A50 |
EN ISO 17632-A-T 42 2 P M 1 H5 | AWS 5.20 E71T-1M | 1,2mm, 1,4mm, 1,6mm | |
Premiarc DW-329AP |
EN ISO 17663-A T 22 9 3 N L P M21 1 | AWS A5.22 E2209T1-4 | 1,2mm | |
Familiarc MX-100T |
EN ISO 17632-A-T 42 2 M C/M 1 H5 | AWS A5.18 E70C-6C/6M | 1,2mm, 1,4mm, | |
Premiarc DW-309L |
EN ISO 17663-A T 23 12 L R C1/M21 3 | AWS A5.22 E309LT0-1/4 | 0,9mm, 1,2mm, 1,6mm | |
Premiarc DW-309LP |
EN ISO 17663-A T 23 12 L P C1/M21 3 | AWS A5.22 E309LT1-1/4 | 0,9mm, 1,2mm | |
Cromacore 2507 |
EN ISO 17632-A T 46 6 1,5 Ni P M 1 H5 | AWS A5.29 E81T1-K2M | 1,2mm | |
Elgacore DWA 55L |
EN 758 / 12535 | AWS A5.28 / A5.29 | Re: 550 MPa Rm: 620 MPa A5: 27 % CV: -60°C · 75 J | 1,00 - 1,60 mm |
Cromacore DW 308L |
EN 12073 - T 19 9 L R M/C 3 | AWS 5.22 - E 308 L T0 - 4/ - 1 | Rp 0,2%: 400 MPa Rm: 570 MPa A5: 42% CV: -20°C 43 J | 0,90 - 1,20 mm |
Elgacore DWA 55 Ni |
EN 758 / 12535 - T 46 6 1Ni P M 2 H5 | AWS A5.28 / A5.29 - E 81T1 - Ni 1 M J | Rp 0,2%: 550 MPaRm: 610 MPaA5: 28% CV: -60°C 75 J | 1,20 mm |
Elga G2 |
EN 12536 0 O II | AWS A5.2 R 60 | Rp 0,2%: 300 N/mm²Rm: 390 N/mm²A5: 20 % CV: 20°C > 50 J | 2,00 - 5,00 mm |
Cromarod 625-170 |
EN ISO 14172 / E Ni 6625 | AWS A5.11 - 97 / E NiCrMo – 3 | Rp 0,2%: 450 N/mm² Rm: 780 N/mm² A5: 33 % | 2,50 - 4,00 mm |
Elga G3 |
EN 12536 O III | AWS A5.2 R 60 | Rp 0,2%: 310 N/mm²Rm: 400 N/mm²A5: 22 % CV: 20°C > 50 J | 2,00 - 3,00 mm |
Cromarod 625 |
EN ISO 14172 / E Ni 6625 | AWS A5.11 - 97 / E NiCrMo – 3 | Rp 0,2%: 490 N/mm² Rm: 760 N/mm² A5: 35 % CV: 20°C • 75 J -196°C • 40 J | 2,50 - 4,00 mm |
Cromarod 82 |
EN ISO 14172 / E Ni 6182 | AWS A5.11 - 9 / E NiCrFe - 3 | Rp 0,2%: 450 N/mm² Rm: 650 N/mm² A5: 40 % CV: -196°C • 60 J | 2,50 - 3,25 mm |
Ostatní